Product Name/English Name：N,N'-Methylenediacrylamide

CAS：110-26-9

Molecular Formula：C₇H₁₀N₂O₂

Article No.：J0008

Structural Formula：

Product Introduction

N,N'-Methylenediacrylamide is a widely used crosslinking agent with stable quality, high purity, and good performance. It belongs to the thickening agent and adhesive of acrylamide. It is used in Textile manufacturing to produce thickening agent and adhesive, in oil exploitation to produce plugging agent. It is also widely used in various fields such as leather chemicals and printing.

Application of N,N'-Methylenediacrylamide

As China's oil development enters the mid to late stage, the demand for improving the recovery rate of old oil fields is becoming increasingly urgent. The formation of many large pores and microcracks in the reservoir exacerbates the heterogeneity contradiction of the reservoir, resulting in lower oil recovery efficiency. In order to solve this problem, various water plugging and profile control agents are used to plug the high permeability area in the formation. Pre crosslinked gel particle (PPG) is a widely used water plugging and profile control agent at present. Because of its chemical structure, there are a large number of hydrophilic groups, it can absorb water several to hundreds of times its own mass. PPG can absorb water and swell under formation conditions, achieving effective sealing of high permeability reservoirs, improving formation heterogeneity, increasing the sweep efficiency of subsequent water flooding, and thereby improving oil recovery. However, the strength of conventional PPG will significantly decrease after water absorption and swelling, resulting in its susceptibility to shear failure under formation pressure, which greatly affects the water plugging and profile control effect of PPG. Therefore, CN116162206A patent develops a high-strength gel particle and its preparation method. The high-strength gel particle is mainly prepared from biomacromolecules, comonomers, organic crosslinkers, nano crosslinkers, initiators and other raw materials. The specific preparation method is:

Add 5g of chitosan, 2g of acrylamide, 3g of N, N-dimethylacetamide, 1g of N-vinylpyrrolidone into 25g of deionized water, mix evenly, then add 0.05g of N, N-methylenebisacrylamide and 0.5g of nano crosslinking agent solution (concentration of 10wt%) made in the laboratory, add 0.1g of initiator after 30 minutes of nitrogen and oxygen removal α-Ketone Glutaric acid, and then photoinduced reaction for 12 hours to obtain pre crosslinked hydrogel; Then, the hydrogel is immersed in 1mol/L calcium chloride solution for 48 hours to obtain multiple crosslinked hydrogel; Finally, after drying, crushing and screening, high-strength and multi crosslinked gel particles are obtained.

Compared with existing technologies, the introduced biological macromolecules form coordination cross-linking with metal cations, and the copolymerized monomers can self crosslink to form relatively uniform cross-linking points during the free radical polymerization process. Organic cross-linking agents also serve as organic cross-linking points, enabling other introduced monomers to crosslink to form network structures and construct chemical cross-linking points; At the same time, the surface of the nano crosslinking agent contains multiple vinyl functional groups, which act as nano crosslinking agents and reinforcing agents, endowing the crosslinking system with more excellent performance.

References

CN116162206A  A high strength gel particle and its preparation method.